iron mesh screen

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Flexibility because the wire is different from other stainless steel raw materials, it is low density so in the flexibility of the appropriate excellent, it can be described according to people’s fantasy into all kinds of different shapes. Some large enterprises will buy hook flower net products, its reasons are no more than two, one is to prevent people outside the enterprise to walk around at will, the second is to advance the whole image of the enterprise. Therefore, under the premise that the protection requirements are not high, galvanized hook net can play a role in its use, the appearance of flexible hook net is settled to the use of address, from a distance and look at it like a work of art quite appreciate the meaning.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

The reason for the bridge reinforcement is that the bridge durability function is poor and aging, through the steel wire mesh reinforcement, can prolong the service life of the bridge, to avoid the bridge cracks, collapse and other phenomena, steel wire mesh in the bridge reinforcement anti-crack engineering can play an obvious effect, improve the construction speed of the project, enhance the concrete anti-crack function, sum up the economic benefits.

Hot wire plating adopts zinc-free slag to add hot molten zinc and galvanizing, which avoids the traditional heating process, radiates 1653 hot molten zinc on surface 4102 of zinc liquid surface, and reduces the high temperature oxidation of zinc liquid surface. At the same time, the heating body is in contact with the zinc liquid, and the heat is directly transferred to the zinc liquid. The utilization rate of heat energy can reach more than 90%, and the heat radiation on the zinc liquid surface is reduced.