framing nails coil

3cm electric welding net refers to the square hole net of 3cm mesh, galvanized net, impregnated plastic wire mesh, metal mesh, screen. Wide 0.914 m, 1.02 m, 1.2 m, 1.5 m, 1.8 m, length of each volume in 18 to 30 m, welded wire mesh is a wire drawing, wire with advanced welding equipment on the line of welding and become, can be cold zinc, hot dipped galvanized after welding, jinsu anticorrosive processing, also can use the black wire or change wire drawing, galvanized wire, stainless steel wire welding forming, The electric welding mesh is firm, the mesh surface is smooth, is widely used in construction, breeding, isolation, handicraft manufacturing, filtration, mechanical protection, animal fencing and other aspects, according to the demand can be customized electric welding mesh coil, can also be cut into electric welding mesh.

3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.