parrot aviary mesh

Poor pretreatment before electroplating; Bath temperature is too low; Poor quality additives or excessive additives and organic impurities can cause poor bonding. The quality of the additive also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the lattice and create stress, causing the coating to blister.

3, galvanized wire galvanized process

Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot-dip galvanized iron wire is widely used in the manufacture of wire mesh, highway guardrail and construction projects. With thick coating, corrosion resistance, strong coating characteristics. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire.

The entire steel surface is protected, and the melted zinc is easily coated evenly, whether in the interior of the pipe fitting in a depression, or in any other corner where the coating is difficult to access. The hardness of galvanized coating is greater than that of steel. The Eta layer of the upper layer of Z is only 70 DPN hardness, so it is easy to be dented by collisions. However, the hardness values of the lower layer of Zeta layer and delta layer are 179 and 211 DPN respectively, which are higher than that of the iron material of 159 DPN. Therefore, its impact resistance and wear resistance are quite good.

The main factors causing metal rust: relative humidity of the atmosphere at the same temperature, the percentage of water vapor content and water vapor saturation content in the atmosphere, known as relative humidity. Under certain relative humidity, the corrosion rate of metal antirust oil is very small, but higher than the relative humidity, the corrosion rate increases suddenly. This relative humidity is called the critical humidity. When the humidity in the atmosphere is higher than the critical humidity, the metal surface will appear water film or water droplets, if the atmosphere contains harmful impurities, dissolved in the water film, water droplets, electrolytes and aggravate corrosion.