22 caliber concrete anchors

First, galvanizing can enhance the corrosion resistance of the product. Zinc has high potential and excellent anodic protection. When the surface of the product is galvanized, zinc will have an electrochemical reaction with oxygen and water in the environment, thereby forming a dense zinc oxide protective film, preventing the metal from further contact with external oxygen, water and other substances, slowing the corrosion rate of the metal. Galvanized products after wire drawing processing, because the surface of the product has a more dense zinc oxide protective film, it can better resist external corrosion and improve the corrosion resistance of the product.

Galvanized iron wire is divided into hot galvanized wire and cold galvanized wire, the use of low carbon steel wire processing, after drawing molding, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes. Good toughness and elasticity, zinc content can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Galvanized iron wire can be cut off the tie wire used in the building, the length of 20cm 30cm 40cm, can be cut off according to requirements.

According to the different requirements of the industry, different weights of alloy ingots are put in the smelting furnace according to the standard, such as weaving, Ming, paper, lang, silicon, etc., and the data out of this smelting is called gold ore iron. Iron has gray iron, white iron and the above-mentioned gold, they have different characteristics, so in the industry according to their different characteristics to transport and selection. For example, in gray iron, its carbon exists in iron ore in graphite condition, the crack is often gray, soft and strong, simple filtering, suitable for casting.