perforated screen sizes

The service condition and service life of electro galvanized iron wire or component are closely related to the thickness of electroplated coating. The more strict the conditions of use and the longer the service life, the thicker the layer of galvanized iron wire required. Different products, according to the specific environment (temperature, humidity, rainfall, atmospheric composition, etc.) to determine the expected service life of the coating thickness, blind thickening will cause all kinds of waste. But if the thickness is insufficient, it will not reach the expected service life requirements. Different manufacturers, according to their own equipment conditions, in the case of determining the plating, the first preparation of a more complete and reasonable process flow, clear plating parameters, control plating solution concentration, standard operation.

The hook mesh is a good material for flood control and flooding. Can also be used for arts and crafts manufacturing, mechanical equipment transport network mountain beautification network – high strength steel wire grid (hook mesh, diamond mesh) hook mesh mountain protection application principle, hook mesh interests, mesh uniform, flat, woven concise, hook woven, beautiful and generous, net, net width, wire diameter is thicker, not easy to corrosion, long life, strong usefulness.

3. The surface adhesion of stainless steel pet cage contains acid, alkali and salt substances (such as alkali and lime water splashing on the decoration wall), which causes local corrosion.

Ordinary blades installed on the walls of the barbed wire fence height in two metres of general construction cost in more than a dozen yuan a metre, but if the prison on the height of the wall construction modest have already reached the four or five meters so that every one meter of the cost of construction in 30-40 yuan, mainly because the work high above the risk is bigger. The construction cost is different, but the price of the blade barbed rope is the same. The construction cost is often higher than the product. In this way, the blade barbed rope factory recommends customers to use the blade barbed rope with better quality to avoid the tedious time and cost of subsequent removal and installation.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

The large roll of galvanized wire is like the literal meaning, is wrapped in a layer of zinc on the surface of low carbon steel wire material, beautify the appearance at the same time, but also improve the corrosion resistance of galvanized wire. Zinc dissolves easily in acids and also in bases, so it is called a bi-soluble metal. Zinc changes little in dry air. In moist air, a dense basic zinc carbonate film forms on the surface of zinc.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

The technical term “galvanized” means that metal has been specially treated with zinc. Essentially, the wire is covered with a very thin layer of zinc. It is this thin layer of zinc that gives galvanized wire its many properties. Galvanizing can be done by dipping wire into a pool of zinc or by electroplating.

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.