2x4 cattle panel

Wire rod to stop normalizing or soxaustenitizing treatment, large specifications with spheroidizing annealing instead. In the middle, especially before the waste product drawing process of thermal disposal throughout the selection of soxaustenitizing disposal. Decarbonization should be prevented during thermal disposal. Sulfuric acid or hydrochloric acid pickling was used to remove the oxide sheet after hot treatment. Coating (see lubrication carrier) can be dipped in lime, phosphating, borax disposal or copper plating.

Hot plating wire can generate thicker coating, and there are both pure zinc layer and iron zinc alloy layer, so the corrosion resistance is better. The production power of hot dip galvanizing is particularly high, and the duration of the parts in the hot dip galvanizing tank usually does not exceed lmin. Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. To plate, tape, wire, tube and other profiles plating, automation degree is higher.