In fact, although galvanized hook net is a useful material for iron products, but fundamentally speaking, modern hook net through continuous transformation and improvement, even if it seems to be not useful products, also have a role in its use, here we can turn our attention to people abandoned galvanized hook net.

With a large pickpocket for the steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for steel wire galvanized; Zinc pot steel wire outlet in 30 minutes, with the pickpocket back and forth, until the large, floating zinc residue into brown yellow, real zinc ash, zinc ash surface. The zinc ash taken out should be brown yellow real zinc ash, zinc surface, effectively reduce the zinc consumption. This is one of the biggest measures to reduce zinc consumption, and it is a real problem, which has not been solved for many years.

Galvanizing can be done by zincate galvanizing or chloride galvanizing. Appropriate additives should be used to obtain a coating that meets the requirements of this standard. Light treatment should be carried out after light plating. The parts that need to be dehydrogenated for passivation should be passivated after dehydrogenation. Before passivation, 1%H2SO4 or 1% hydrochloric acid should be applied for activation for 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.