black annealed binding wire

In addition, before the steel wire enters the zinc liquid, covered with a layer of insulation material containing zinc oxide reducing agent, can reduce the heat loss and zinc ash floating. In addition, adding zinc-5% aluminum-mixed rare earth alloy to the zinc solution, when the zinc solution contains 0.002%-0.005% aluminum mass fraction, can obviously increase the brightness of the zinc layer, and prevent the zinc solution surface oxidation caused by excessive zinc ash.

Similar to two materials in the coating part melting together, and coating thickness can reach 100 microns, so high corrosion resistance, salt spray test 96h no problem, equivalent to 10 years under the usual environment; Cold galvanizing is electroplating at room temperature. Although the thickness of the coating can also be controlled, the binding strength and thickness of the coating are relatively low, so the corrosion resistance is poor.