The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

(3) For some use of special paint spraying should be baked, of course, depending on the size of the area, small can be placed in the oven, large can only be dried first, and then to dry parts for processing, lock baking, if other circumstances can only use high temperature tools bit by bit baking. The products that can be baked in the oven should be leveled at room temperature for 15 to 30 minutes, baked at a low temperature of 60 degrees Celsius for half an hour, and then baked at the reserved baking temperature for one and a half hours, and then cooled down.

Hot dip galvanized iron wire using high quality carbon structural steel, after drawing, galvanized iron wire processing. Hot-dip galvanized iron wire is widely used in the manufacture of wire mesh, highway guardrail and construction projects. With thick coating, corrosion resistance, strong coating characteristics. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire.