The composition of hot dip galvanizing layer is composed of hot dip galvanizing layer, which is composed of iron zinc alloy between iron matrix and surface pure zinc layer. The shape of the workpiece is formed by the iron zinc alloy layer in hot dip, so that the iron and pure zinc layer touch outstanding. When the iron workpiece is immersed in a molten zinc solution, the initial zinc and iron (body) are formed at the interface. This is a crystal made up of zinc atoms in the solid metal iron. When two metal atoms are fused together, the gravitational force between the atoms is very small.

Hot dip galvanized wire is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, and the matrix metal forms the infiltration layer, the corrosion resistance is good, the outdoor environment of hot dip galvanized wire can be maintained for decades.

If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.