10 galvanized wire

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

On the highway, the barbed wire protective net is generally used to prevent people and animals from crossing the highway at will, so as not to interfere with driving and reduce accidents, as well as effectively prevent illegal occupation of highway land and other issues of traffic safety facilities. There are many forms of barbed wire protective nets, commonly used are metal, woven nets, barbed wire and evergreen green gracilaria. In the densely populated areas set up metal woven net, people and animals are less sparse areas of the form of barbed wire, in the toll station, service area and other sections of the structure of hedge and barbed wire. In the past two years, considering the aesthetic problem, some highways in the Pearl River Delta region adopted the fruit plastic spot welding mesh (usually said guardrail mesh), the barbed wire protective mesh is more beautiful, but also durable, the overall effect is good, but the construction requirements are higher, more expensive. General sections should not be used, in the city center, scenic spots or strong requirements for beauty of the section available.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.