Stainless steel blade barbed wire production process is similar to galvanized blade barbed wire production process, usually according to the mold to determine the size of the blade.

In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

The advantage of galvanized iron wire after annealing: after annealing increases the elongation of the iron wire. Makes the product softer and increases the range of application. After electric galvanizing hot dip galvanizing. Copper electroplating is widely used and screen production. Galvanized iron wire is a soft iron wire product processed by low carbon steel wire through cold drawing, heating, constant temperature, and even heat preservation. Generally, the quality of ordinary galvanized iron wire will be relatively soft, the softness is relatively balanced, and the color is consistent. It is mainly used in construction, mining, chemical industry and so on.

There are many kinds of zinc plating solution, which can be divided into plating solution and no plating solution according to its properties. The galvanized liquid has good dispersion and covering property, the coating crystal is smooth and fine, the operation is simple, the application range is wide, and the long-term use is in the production. However, due to the toxic substances contained in the plating solution, the gas escaping from the plating process has great harm to the health of workers, and the waste water must be treated strictly before discharge.

Non-proportional extension strength: It is mainly for hard steel without yield point. It is defined as the stress where the residual elongation of the standard distance part reaches 0.2% of the length of the original standard distance.