electro galvanized coil

Life said “wire”, in fact, is “low carbon steel wire”, carbon content in 0.2% below. The surface is usually coated with zinc coating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. Life said “steel wire”, is the carbon content of about 0.6% of the “carbon steel wire”, or carbon content of about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. The use of words such as winding ordinary spring and so on.

Cold galvanized by electrolytic action to metal and other materials surface attached to a layer of metal film, so that the surface of the material uniform texture, anti-corrosion wear, appearance is more beautiful. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other “rough” workpiece long-term rust prevention.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

When this ore is specially refined into metallic iron, carbon, silicon, manganese, and other elements are added to it, so that the refined material is called general pig iron, which is also the material for the initial grade. According to the different requirements of the industry, different weights of alloy ingots are prepared in the smelting furnace according to the standard, such as weaving, Ming, paper, Lang, silicon, etc., and this smelting material is called combined gold ore.

Hot dip galvanized steel wire surface smooth, smooth, no cracks, joints, thorns, scars and corrosion, galvanized layer uniform, strong adhesion, corrosion resistance lasting, toughness and elasticity is excellent. The tensile strength should be between 900Mpa-2200Mpa (wire diameter Φ0.2mm-Φ4.4mm). The number of torsion (Φ0.5mm) in more than 20 times, repeated bending should be more than 13 times. The thickness of galvanizing is thin, usually only 3-15 microns, bright, smooth, beautiful appearance, poor corrosion resistance, generally a few months will rust.