60 micron mesh

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging.

If using common galvanized barbed wire due to the influence of climate and environment, will accelerate the corrosion rate of barbed wire lower utilization rate, so use stainless steel barbed wire in coastal areas is the best choice, if it is the environment is dirty it is recommended to use stainless steel barbed wire of nickel content in the highest 316 l, so that you can extend the service life, greatly enhance the protective effect.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

This method is generally the use of hot rolled laminated plate as raw material, the annealed steel plate is first sent to the pickling workshop, with sulfuric acid or hydrochloric acid to remove the surface of the steel sheet oxygen hot galvanizing method. After pickling, the steel plate immediately enters the tank to soak and wait for galvanized, which can prevent the reoxidation of the steel plate. After pickling, water cleaning, squeeze dry, drying, into the zinc pot, the temperature has been maintained at 445-465℃.

The distance between the adjacent two thorn rope installation do not know whether you have noticed? Careful observation can find that its spacing is not the same, the thorn rope factory for customer consultation when asking the installation height of the reason.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

The silver powder is actually a mixture of aluminum powder and polymer after painting the film, the film is brittle, easy to appear adhesion problems, and corrosion resistance is also slightly poor. Galvanizing refers to the surface of metal, alloy or other materials coated with a layer of zinc to play the role of beautiful, rust prevention and other surface treatment technology. Zinc dissolves easily in acids and also in bases, so it’s an amphoteric metal. Zinc changes little in dry air.

Fence use: The use of the fence is generally one meter two to two meters a height of the impregnated welding mesh, mesh mostly 6cm, wire diameter from 2mm to 3mm.