aviary wire mesh

Because of the pre-tension given to the packaging and binding of galvanized wire, it has the excellent characteristics of low relaxation value, small stress loss, good stability after loading, not easy to deformation, no fracture, strong elasticity, ordinary steel lines and rebar are difficult to compare. The use of advanced galvanized finishing process, therefore, the use of hot-dip galvanized steel wire construction, not only good corrosion resistance, but also beautiful and generous. The product has the characteristics of smooth surface, high dimensional accuracy, good uniformity of zinc layer and strong adhesion.

There is as far as possible not to show the trace of the application of wire, wire wound flower stems should be wrapped with green or brown tape, in order to cover the trace of the use of wire, in the use of wire modeling can make the drooping flower head raised, and the flower head reinforcement, for herbs and other flower material soft plants, can make the stalk straight. Wire shearing method: if you want to cut the wire, the wire should be straightened and then cut, can not bend the wire, fold and then cut, otherwise, the wire cut is not straight, will bring a small hook, affect the use.

Galvanized wire is immersed in heated molten zinc, the production speed is fast, the coating is thick but uneven. The thickness of 45 microns allowed by the market, the color is dark, the consumption of zinc metal is more, and the matrix metal is formed into an infiltration layer, and the corrosion resistance is good. The hot dip galvanizing can be maintained for decades in the outdoor environment.

Galvanizing can be done by zincate galvanizing or chloride galvanizing. Appropriate additives should be used to obtain a coating that meets the requirements of this standard. Light treatment should be carried out after light plating. The parts that need to be dehydrogenated for passivation should be passivated after dehydrogenation. Before passivation, 1%H2SO4 or 1% hydrochloric acid should be applied for activation for 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.