1 weld mesh

(4) Stop the use of more than two strands of galvanized iron wire around the operation method.

Hot dip galvanized wire 5#-28#, including 500-1000 kg large plate hot dip galvanized wire. The hot dip galvanized wire we produce is made of national standard low carbon steel wire by drawing molding, pickling rust removal, high temperature annealing and other processes. The product has the characteristics of strong flexibility and good plasticity. The amount of zinc can reach 360 g /m2, which is welcomed by customers.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

Hot-dip galvanized wire is widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transmission, shipbuilding and other industries. It has been widely used in recent years in agricultural fields such as agricultural medicine sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and so on.

A pet carrier can be used as an indoor or outdoor pet house. The dog cage is equipped with a fixed food basin and water fountain, and the foot plate pet cage rubber pad has bayonets on four sides to be splintered. It can be spliced, cut and disassembled according to the size of the cage. It is convenient and easy to clean. It can solve the problem of pinching the feet of the puppies in the ordinary cage and prevent the puppies from causing adverse reactions in the development. The dividers are breathable and comfortable, and can be used as heat shields for pets in summer. A puppy with small feet, no feet, no pinching.

Large roll galvanized wire is simply galvanized iron wire, usually used wire is often visible, because iron is very easy to be corroded and rusted, so it is necessary to put a layer of other not easy to rust metal plating in the outer layer, to achieve the effect of corrosion resistance and rust resistance, the effect of zinc can do more. Therefore, many customers often require hardware factories to produce galvanized iron wire, which requires the use of galvanized iron wire equipment.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

3. Acid activation acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts, without excessive corrosion on the matrix.

Hot dip galvanized coating is also relatively thick, but there is an uneven situation, for example, the thickness of the thin is only 45 microns, thick can reach 300 microns or even thicker, the color of this product is relatively dark. There is also a lot of zinc consumed in the production process. Zinc will form an infiltration layer with the metal. Its advantage is that it has good corrosion resistance. Electrogalvanizing, it is through the plating tank in the zinc one-way plating on the outside of the metal products, this way of making products is relatively slow, but its thickness is more uniform.