3) wire surface coating: some businesses say their pet cage with what stainless steel, in fact, we also know that the price of stainless steel will not be very cheap, most of the cage surface coating is a layer of anti-rust coating, the material is mainly PE powder, but some color is different. The cage of good quality will be cleaned before coated with PE powder, and then baked at a high temperature of 200 degrees, so that PE powder can stick firmly on the wire.

Galvanized wire hexagonal mesh material: cold galvanized wire, hot galvanized wire, to draw wire

Annealing is to restore the plasticity of wire, improve the tensile strength of wire, hardness, elastic limit, etc., the wire after annealing is called annealing wire. In the production process of annealing wire, it is very important to ensure the quality of the finished wire, make the wire have certain strength and suitable degree of soft and hard. The annealing temperature is between 800 ℃ and 850℃, and the length of furnace tube is lengthened appropriately for enough holding time.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Galvanized iron wire is very common in practical application, some people think that galvanized iron wire will not rust, in fact, it is not. Metal corrosion is caused by the chemical or electrochemical action of the surrounding medium. According to different media, it is divided into atmospheric corrosion, soil corrosion, seawater corrosion, bacterial corrosion and so on. Atmospheric corrosion is more common, because metal products in the process of processing, transportation and storage, when in contact with the atmosphere, there are always atmospheric corrosion conditions.

That said, it can always deform by pulling hard without changing its integrity, so cold drawing has usually reached a limit, which is not a problem, because without this property it increases hardness, which is the desired effect. Cold wire drawing encountered more rain, when the climate is wet, easy oxidation and rust. Therefore, in the storage process should pay attention to avoid rust.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

Hardness is a commonly used property index in mechanical properties of metal materials. The iron wire factory introduces a fast and economical test method for hardness testing. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad. In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting.

Specific requirements for the safety of galvanized wire production: clean up all tools and other objects that hinder production in the galvanized wire production environment. Operators in the pickling process, pay attention to the action should be careful, not careless, into the pickling tank must be handled lightly, to prevent splashing on the body. When adding acid, the acid must be slowly poured into the water. It is forbidden to pour the water into the acid, so as to prevent the acid from splashing out and hurting people. Do not hurt yourself or others.

Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.