metal perforated mesh

First, the commonly used stainless steel plate is divided into two types of 201 and 304, the actual composition of the Nestor cage is different, 304 stainless steel Nestor cage quality is better, but the price is expensive, 201 is worse. Anping 304 for imported stainless steel plate, Anping 201 for domestic stainless steel plate.

The key and important parts with tensile strength greater than 1034Mpa should be relieved of stress at 200±10℃ for more than 1 hour before plating, and the carburized or surface hardened parts should be relieved of stress at 140±10℃ for more than 5 hours. The cleaning agent used for cleaning shall have no effect on the binding force of the coating and no corrosion on the substrate. Acid activation Acid activation solution should be able to remove corrosion products and oxide film (skin) on the surface of parts without excessive corrosion on the matrix.

In sulfur dioxide, hydrogen sulfide and Marine atmosphere, zinc corrosion resistance is poor, especially in the high temperature and high humidity atmosphere containing organic acid, galvanized wire galvanized layer is easy to be corroded. The uniformity of the galvanized layer on the surface of galvanized wire and the color of galvanized wire, the galvanized layer on the surface of high-quality galvanized wire is uniform, zinc adhesion is good, and the color is white, there is no leakage plating and rust points and other problems.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

(3) anti-freezing, residential protection, landscaping protection;