crimped brass wire mesh

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

First of all, the protective layer of zinc-iron alloy can prevent the steel wire from being corroded by oxidation. The zinc metal reacts with water and oxygen to form a dense zinc oxide layer, which forms a physical barrier to prevent oxygen and water from entering the inside of the steel wire, reducing the chance of corrosion. Compared with ordinary steel wire, hot-dip galvanized wire is more resistant to corrosion in humid, high humidity or corrosive environments such as acid and alkali, so it is more durable.