Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Because the coating obtained is thicker, hot-dip galvanizing has very good protective function than electric galvanizing, so it is an important maintenance coating for iron and steel parts in strict working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding and other occupations. In the field of agriculture, such as pesticide irrigation, greenhouse and construction industry such as water and gas transportation, wire casing, scaffolding, Bridges, highway guardrail and other aspects, it has been widely used in these years.