thin drywall screws

Electro galvanizing shaft wire direct is in the electroplating tank through the current unidirectional zinc gradually plated on the metal surface, production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, electric galvanizing has lower production cost. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanized shiny hair white.

Large roll galvanized wire is the use of low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes, in the use of is more widely. The temperature of large roll galvanized wire for electroplating should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Positive twist: Twist two or more pieces of wire into a double wire rope and then wrap the wire around the double wire. It’s called a positive twist cord which is a common double strand cord.

After annealing, the extension rate of galvanized wire is increased, making the product more soft and increasing the scope of application of galvanized wire. After electric galvanized hot galvanized, electroplated copper and other widely used screen production. Building reinforcement binding with galvanized wire mesh braided with the first after plating, plating and other methods, after treatment of galvanized wire mesh or steel wire mesh, has good corrosion resistance, oxidation resistance characteristics, can be used in construction, petroleum, chemical, aquaculture, garden protection, food processing and other industries reinforcement, protection and heat preservation.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.