On the highway, the barbed wire protective net is generally used to prevent people and animals from crossing the highway at will, so as not to interfere with driving and reduce accidents, as well as effectively prevent illegal occupation of highway land and other issues of traffic safety facilities. There are many forms of barbed wire protective nets, commonly used are metal, woven nets, barbed wire and evergreen green gracilaria. In the densely populated areas set up metal woven net, people and animals are less sparse areas of the form of barbed wire, in the toll station, service area and other sections of the structure of hedge and barbed wire. In the past two years, considering the aesthetic problem, some highways in the Pearl River Delta region adopted the fruit plastic spot welding mesh (usually said guardrail mesh), the barbed wire protective mesh is more beautiful, but also durable, the overall effect is good, but the construction requirements are higher, more expensive. General sections should not be used, in the city center, scenic spots or strong requirements for beauty of the section available.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, filtration test, and then take a small amount of electroplating solution, with zinc powder treatment after the test, check the problem is solid particles or copper, lead and other foreign metal impurities caused by. One by one, it’s not hard to find the cause of the problem. Galvanized iron wire coating blister, poor adhesion.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

The protective duration of the galvanized layer of large roll galvanized wire is closely related to the thickness of the coating. Generally speaking, in relatively dry main gas and indoor use, and in harsh environmental conditions, the thickness of galvanized layer needs to be very high. Therefore, the environmental impact should be considered when choosing the thickness of galvanized layer. After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance.