75 x 75 weld mesh

In use, it can be well used to control the degree of softness and hardness in the annealing process, mainly used for binding silk and binding wire in the construction industry. Its use is not limited to handicrafts, of course, in the construction industry is also widely used. In the early days, the lanterns were made with wire outside and proper candles were placed inside. People hung them in front of the door and it was very beautiful to go up at night.

One is the frame isolation net, guardrail net with frame, frame using material cold plate belt welded into the square tube, usually 2*3 thickness 1.2 thick, the middle for low carbon steel wire welding mesh, wire diameter can choose another welding aperture can also choose, for example, customers want good quality long service time, you can choose thick wire diameter, small welding aperture, Such mesh is not only high quality, but also long service life, customized mesh and frame after welding, surface treatment to reach the customer needs of goods.

First of all, we need to pay attention to the material of the barbed wire, because the galvanized barbed wire itself includes cold plating and hot plating. The properties and prices of the two are obviously different, and it is easy to be confused by a little negligence.

There are two varieties of steel grid plate is pressure welded steel grid plate and pressure lock steel grid plate, in many people’s eyes, these two products belong to the same variety, in fact, there are still great differences between them in many places.

There is no need to carry out daily maintenance and maintenance when in use, which can not only save a lot of time, but also reduce the cost, but also has good stability, strong corrosion resistance, greatly extend the service life. According to the different technology is divided into different types, can be selected according to their own needs, has better flexibility and elasticity. The main function of annealing wire is to control its hardness, when the annealing wire is made of steel wire.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.