No matter how good the quality of hot-dip galvanized barbed rope is, it is only attached to the surface of the wire with galvanized layer, and with the cause of chemical reaction, the zinc layer on the surface will gradually lose its effect because of oxidation reaction, which is more prominent in the humid area of the environment. And because, after all, the wire will rust, so the quality of hot-dip galvanized barbed rope is certainly not up to the level of stainless steel barbed rope.

Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it is also necessary to conduct reasonable post-processing to avoid affecting its use effect. Of course, when the black iron wire is galvanized, it is also necessary to ensure the thickness of the galvanized layer, so that it can also reduce the possibility of rust. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.