“Wet” hot dip galvanizing is also called “molten solvent method” hot dip galvanizing. Iron and steel workpiece through degreasing, pickling and cleaning, it is necessary to set in a special box above the surface of the molten zinc in the “molten solvent” (also called cosolvent), and then into the zinc liquid to galvanized. The molten solvent is usually a mixture of ammonium chloride and zinc chloride, but also other chlorine salts.

The service condition and service life of galvanized iron wire or components are closely related to the thickness of the coating. The more strict the use conditions and the longer the service life, the thicker the required layer of galvanized iron wire should be. Different products, according to the specific environment (temperature, humidity, rainfall, atmospheric composition, etc.) to determine the expected service life of the coating thickness, blind thickening will cause all kinds of waste. But if the thickness is insufficient, it will not reach the expected service life requirements. Different manufacturers, according to their own equipment conditions, in the case of determining the plating, the first preparation of a more complete and reasonable process flow, clear plating parameters, control plating solution concentration, standard operation.

Three is to do a good job of galvanized silk product production site clean and tidy, in accordance with the scientific method of operation to operate the production, the operator should wear the required dress. If it is hot dip galvanized wire products, we must do a good job of passivation treatment, will be able to effectively prevent discoloration, prolong the method of discoloration, can solve the problem of discoloration.

When large rolls of galvanized wire are used to bind and reinforce the goods, corresponding binding methods should be selected according to the fastening node conditions of the strengthened goods, such as opening binding, opening binding, insertion binding and so on. The insulation layer of semi-hard and soft insulation products shall be based on the diameter of the steel pipe and the size of the equipment. Large rolls of galvanized wire or glue are tied together with a width of 60mm. The binding interval of semi-hard insulating products shall not exceed 300 mm; The larger length of felt and cushion shall not exceed 200mm, and the number of belts shall not be less than 2.

What Is FRP Grating?