There is no adhesion test of powder spraying or fluorocarbon spraying on packaged galvanized wire, but there are two points for reference: first, in sealed or air-free environment, non-metallic volatiles can corrode zinc coating; Second, zinc at higher than 230 degrees (c) will cause the matrix metal brittle. And powder spraying and fluorocarbon spraying are to be baked at a higher temperature and in a sealed environment, causing rapid corrosion of zinc, resulting in loose corrosion film resulting in coating adhesion decline, and even lead to (matrix) steel wire brittle situation may exist.

In moist air, a dense basic zinc carbonate film forms on the surface of zinc. Zinc coating belongs to the anodic coating, it is mainly used to prevent the corrosion of steel, its protective performance and the thickness of the coating is very important. The protective and decorative properties of zinc coating can be improved significantly after passivation treatment, dyeing or coating with light protection agent.

Cattle net in the outdoor use of a long time will inevitably show rust corrosion, this time the use of cattle net life depends on the maintenance of the product is not in place, we all know that cattle net if long exposure to harsh environment, the service life will be greatly reduced. How long does a normal cattle net last?

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Galvanized wire to galvanized evenly, a body is now its cross section, the second is the longitudinal uniformity. In the actual operation process, such as the jitter of steel wire, the surface scum in the plating pot and other reasons will cause the accumulation of galvanized layer on the surface of galvanized wire, and efforts should be made to solve the problem.