Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Performance characteristics of zinc coating: zinc layer of thick galvanized wire zinc layer crystallinity meticulous, uniform and no gap, good corrosion resistance; The zinc layer obtained by electrogalvanizing is very pure and corrodes slowly in the gas, liquid and fog of acid and alkali, which can effectively protect the steel matrix. Galvanized layer can also be chromic acid passivation treatment into a variety of colors, beautiful and generous, with good decorative; The zinc layer on the galvanized wire has good ductility, can be cold blanking, rolling, bending and other molding without damage to the zinc layer.

Heavy hexagonal net is made of low carbon steel wire galvanized large wire braid, the tensile strength of the steel wire is not less than 38kg/m2, the diameter of the steel wire can reach 2.0mm-3.2mm, the surface of the steel wire is usually protected by hot dip galvanizing, the amount of galvanizing can reach 500g/m2.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Most cattle netting is mechanically woven from highly malleable and corrosion-resistant mild steel wire or PVC coated steel wire. Several commonly used raw materials for the manufacture of cattle net are electrogalvanized wire, hot-dip galvanized wire, Galfan steel wire, ten percent aluminum zinc alloy steel wire and the new type of selenium chromium steel wire.