commercial chain link fence

In the cattle net generally also PVC plastic PVC plastic is coated with a layer of dark green or gray brown plastic mold on the original galvanized steel wire, to avoid the corrosion of the wire diameter, is conducive to the improvement of the wire diameter corrosion prevention and rust prevention function. So the better the raw material, the higher the price. Zinc aluminum alloy cattle mesh is the best metal mesh on the market, the price is higher than hot dip galvanized raw materials. The service life is about 80-90 years, excellent anticorrosion function.

Material: low carbon steel wire (iron wire, stainless steel, aluminum). Features: net average, bright appearance, textile, concise, crocheting, beautiful not stingy. Mesh screen image quality and width, thickness, erosion, long life, applicability. Hook fence nets are tied as consistently as tennis chain fences because they are easily installed. Hook mesh is also called diamond mesh, hook mesh, galvanized hook mesh, plastic wrapped hook mesh, hook mesh is made of hook mesh machine for all kinds of materials of wire hook knitted, can be divided into folding shrink, screw lock two kinds. Material: PVC wire, stainless steel wire, low carbon steel wire, galvanized wire, iron wire, etc.

5, according to the wire diameter thickness to adjust zinc dipping time

The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

Now most people buy barbed rope choose blade barbed rope, why is this? From the material blade barbed wire technology blade gill net is made of hot-dip galvanized steel plate or stainless steel sheet stamped out sharp knife sheet, high tension galvanized steel wire or blade barbed wire stainless steel wire as core wire combination of the resistance device. Because the gill net shape is not easy to contact, so it can achieve excellent protective barrier effect. The primary raw materials of products are galvanized sheet and stainless steel plate.

Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When the galvanized wire out of light plating should be carried out light treatment, the galvanized wire bath to control the temperature. Now the quality level of galvanized wire on the market is not equal, galvanized wire is also called hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities.

There are many important details that need to be paid special attention to during the production of barbed rope or blade barbed rope by the barbed rope factory. If any improper, it will cause unnecessary losses.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

The barbed wire factory will store the inventory of the barbed wire blade in the appropriate place because of the understanding of the product characteristics.