In order to remove the photosynovium and oxide remaining on the surface of galvanized iron wire after drawing or heat treatment, it is necessary to do the surface treatment of galvanized steel wire before plating. The common surface of low carbon steel wire is the light synovium or oxide of animal or vegetable oil; Medium and high carbon steel in addition to contain animal or vegetable oil components.

At the time of production, the annealing wire will be processed according to the performance of the material. According to different needs, the degree of hardness and softness can be changed, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production. In the use of the time does not need to carry out daily maintenance and maintenance, not only can save a lot of time, but also can reduce the cost, but also has good stability, strong corrosion resistance, greatly extend the service life.

In the atmosphere containing carbon dioxide and hydrogen sulfide and Marine atmosphere is not corrosion resistant, in high temperature and high humidity air and contain organic acid atmosphere is small, galvanized layer is also easy to be corroded. In order to make large rolls of galvanized wire on the surface of the deposited layer to the local, remove the surface film layer, surface inclusions and other defects can be found and treated by conventional techniques. Excess foam is caused by soaps and surfactant saponable fats brought into the tank, and moderate rates of foam formation may be harmless.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.