chain link construction fence

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

The material of steel structure will affect the organization and thickness of hot dip galvanized film. For example, high tension steel containing silicon, carbon content is high, easy to react with molten zinc quickly, the result of excessive growth of alloying, will cause a grayish black appearance, but does not affect its corrosion resistance. Or heat treated steel, if its tensile strength exceeds 90kg/mm2, after hot dip operation, easy to reduce its strength, etc.

The use of packaging galvanized wire with the development of industry and agriculture is also expanded accordingly. Therefore, galvanized silk commodities have been widely used in industry (such as chemical equipment, petroleum processing, Marine exploration, metal structure, electric power transportation, shipbuilding, etc.), agriculture (such as irrigation, heating houses), construction (such as water and gas transportation, wire casing, scaffolding, houses, etc.), Bridges, transportation, etc., in recent years. Because galvanized silk products have beautiful surface, good corrosion resistance and other characteristics, its use is more and more extensive.