Galvanized iron wire is divided into hot-dip galvanized wire and cold galvanized wire, using low carbon steel wire processing, after drawing forming, pickling rust removal, high temperature annealing, hot-dip galvanized, cooling and other processes. With good toughness and elasticity, the amount of zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Galvanized iron wire can cut off the tie wire used in the building, the length is 20cm 30cm 40cm, can be cut off according to the requirements.

When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well. Galvanized wire, also known as hot dip zinc and hot dip galvanized, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

Most cattle netting is mechanically woven from highly malleable and corrosion-resistant mild steel wire or PVC coated steel wire. Several commonly used raw materials for the manufacture of cattle net are electrogalvanized wire, hot-dip galvanized wire, Galfan steel wire, ten percent aluminum zinc alloy steel wire and the new type of selenium chromium steel wire.

Second: positive and negative twisting rope cost-effective