The application of black iron wire in the process is mainly through the hot metal billet rolled into 6.5 mm wire rod, and then put it into the wire drawing device into a different diameter line, and then gradually reduce the aperture of the wire drawing disk, cooling and annealing, coating and other processes, made into a variety of different specifications of iron wire, this kind of iron wire and ordinary black iron wire compared, will be softer, Softness is also very uniform, color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: it is an effective way of metal anticorrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into zinc solution melted at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anticorrosion.

The insulation layer of large rolls of galvanized wire and rigid thermal insulation products can be bound with double strands of galvanized iron wire, and the binding interval shall not exceed 400mm. The pipe or corresponding equipment with nominal diameter equal to or greater than 600mm shall stop reinforcement after binding, and the enclosed galvanized steel wire must be winched. The iron or wood rod should be tightened, but the tightening level should be moderate, not too tight or too loose, and not damage the wire. The consumption of wire and steel wire is generally used in drawing process and galvanized disposal.

First, cold galvanized wire production process before treatment. Before galvanizing, a series of pre-treatment work on the steel wire is required, mainly including pickling, dissolution and brine or alkali washing.