perforated stainless sheet metal

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Three is to do a good job in the production of galvanized wire products clean and tidy, in accordance with the scientific method of operation to operate the production, the operator should wear the required dress. If it is hot dip galvanized wire products, we must do a good job of passivation, will be able to effectively prevent discoloration, prolong the method of discoloration, can solve the problem of discoloration.