14 gauge binding wire

Compared with other galvanizing processes, galvanized steel wire has low cleaning requirements before plating. However, under the current trend of increasing the quality level of galvanized layer, some pollutants brought into the plating tank are obviously harmful. Because cleaning galvanized coating wastes a lot of time and reduces production, it is very important to properly clean and effectively rinse the substrate before electroplating.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Cold wire drawing is mainly used in the production of hardened low carbon steel wire, with a diameter of 8 mm steel bar to play a fixed role in the development of the construction industry has played a role in promoting the development of the construction industry, widely used. The bonding and anchorage performance between cold wire drawing and concrete is good. When used in components, the phenomenon of cracking in the anchorage area of components and damage caused by steel wire slip is fundamentally eliminated, and the bearing capacity and anti-cracking capacity of the end of components are improved.