nails for wood to concrete

Generally speaking, there are three kinds of anti-corrosion and anti-rust skills: surface dipping, spraying and surface galvanized, these three ways are to strengthen their anticorrosion ability and resist natural risks, extend their service life. Today we want to talk about the difference between dip plastic hook and galvanized hook.

In use, there is no need for daily maintenance and maintenance, not only can save a lot of time, but also can reduce costs, but also has good stability, strong corrosion resistance, greatly prolong the service life. According to the different process is divided into different types, can choose according to their own needs. With good flexibility and elasticity, the main role of annealing wire is to control its degree of softness and hardness, in the production of annealing wire is made of steel wire, now more used in the construction industry binding use, compared with ordinary wire is also more soft, have better luster.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Some raw materials in the production of unstable processing, the wire itself will exist burr, surface small pits and other local defects. Galvanized steel in galvanized, generally should pay attention to the galvanized layer protection time of galvanized wire, and the thickness of galvanized layer has a great relationship. Generally speaking, when the main gas is relatively dry and used indoors, the galvanized layer thickness of galvanized wires is only 6-12μm, and under relatively harsh conditions, the galvanized layer thickness of galvanized wires needs 20μm, and can be predicted to reach 50μm.

Because of the corrosion resistance of zinc layer, can be applied to all kinds of environment, it is also very convenient to use, has been a more popular hardware products. Galvanized iron wire should pay special attention to the acyl wash, to slowly into the container, to prevent acid sputtering on the body, at the same time prohibit the water into, so it is easy to let the acid out, to learn to handle lightly, stacking should also be firm and neat. It can be widely used in construction, handicrafts and other daily civilian applications.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.