Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

Deoxygenation of boiling steel is incomplete, oxygen content is high, phosphorus and other impurities distribution is uneven, local overspending, aging sensitivity and cold brittle sensitivity are high, hot cracking tendency is added. If unqualified electrode is used, if the content of carbon and sulfur in the weld metal is too high, cracks will occur. For example, when factories use acidic electrodes to weld Q235-A steel, the high carbon fernoganese in the electrode coating will lead to thermal cracks in the weld.