vine support wires

When the large roll galvanized wire galvanizing process coating foaming, first check the bath temperature. If the bath temperature is not low, then strengthen the plating before removing oil, prevent the matrix metal in acid corrosion. If you pay attention to these problems, the foaming phenomenon still exists, it should pay attention to the amount and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, in order to reduce the content of additives, observe whether the foaming phenomenon is improved. If there is still no improvement, it is necessary to check whether the storage period of additives is too long, or whether there are too many impurities in the additives.

The main difference between the two is the carbon content. The carbon content of iron is 2.11 percent or greater, while the carbon content of steel is 2.11 percent or less. The iron carbon alloy with carbon content above 2.11% is cast iron (pig iron), which is basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different. The content of harmful impurities such as sulfur and phosphorus in steel is smaller. Steel wire general color focus, iron wire color light point, white point.

With a large pickpocket for the steel wire, into the zinc liquid before the surface of the zinc ash stirring; Use a small outlet for steel wire galvanized; Zinc pot steel wire outlet in 30 minutes, with the pickpocket back and forth, until the large, floating zinc residue into brown yellow, real zinc ash, zinc ash surface. The zinc ash taken out should be brown yellow real zinc ash, zinc surface, effectively reduce the zinc consumption. This is one of the biggest measures to reduce zinc consumption, and it is a real problem, which has not been solved for many years.