Hot dip galvanized wire 5#-28#, including 500-1000 kg large plate of hot dip galvanized wire. Our hot dip galvanized wire is made of national standard low carbon steel wire after drawing molding, pickling rust removal, high temperature annealing and other processes. The products have the characteristics of strong flexibility, good plasticity and so on. The zinc content can reach 360 g /m2, which is welcomed by customers. We can also provide various specifications of galvanized wire according to customer requirements. The PRODUCTS ARE WIDELY USED IN construction, HIGHWAY fence, TIE-flower, weaving and other industries, mainly used in the manufacture of wire mesh, nail making, highway barrier and construction engineering binding wire, etc.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.