6mm perforated steel plate

2. Zinc layer uniformity: zinc layer uniformity also has an important impact on corrosion resistance. If the zinc layer is not uniform, there are local defects or insufficient thickness areas, it is easy to form corrosion points, resulting in the destruction of the entire zinc layer.

In a rainy climate, it is good to find a place with high dry ground. If there is a rain cloth to hide the rain, so much the better. For field operators, please rest assured that the safety and stability of the mesh, especially in the stacking of paper, slight corrosion will not affect the application.

Hot dip galvanized hexagonal net is made of low carbon steel wire by mechanized braided welding and then by hot dip zinc treatment. The net color is white and shiny, thick zinc layer, uniform mesh, flat mesh surface, solder joint tension resistance, high corrosion resistance. The surface of the steel wire is usually protected by hot-dip galvanizing, and the thickness of the galvanized protective layer can be made according to the requirements of customers. Hot-dip galvanizing hexagonal net is another kind of twisting mesh corresponding to the galvanizing hexagonal net.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.

Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

Large roll galvanized wire is processed by low carbon steel wire rod, through drawing molding, pickling rust removal, high temperature annealing, cooling and other processes. Large roll galvanized wire electroplating temperature should be controlled in 30-50℃. Because of the strong corrosivity of chloride ions in bath, quartz glass heater is generally used. Continuous production does not need heating, but need cooling cooling.

Stainless steel barbed rope is often used in various engineering projects because of its good anticorrosion ability, but it is difficult to be accepted by ordinary families because of its high price. So what material of barbed rope has better anticorrosion ability?

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Defects such as surface film and surface inclusions can be found and treated by conventional techniques in order to remove them locally from the surface of the deposition layer. Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank.

Now many industrial products will be made of stainless steel wire rope material. In order to identify the fake and inferior stainless steel, certain measures and methods can be taken. But many customers do not know what way to identify, listed the following identification methods for you.