Surface coating, surface inclusion and other defects can be removed locally from the surface of the deposited layer before galvanized, which can be found and treated by conventional techniques. Excess foam is caused by the introduction of soap and saponable fatty surfactants into the tank. Moderate foam formation rates may be harmless. The presence of a large number of tiny homogenous particles in the tank, which can stabilize the foam layer, mat with activated carbon to remove surface active substances, or make the foam less stable through filtration, are effective measures.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.