Packing and binding galvanized wire is in the liquid state of zinc, after a messy physical and chemical effect, not only on the steel plated thick pure zinc layer, and also generate a zinc-iron alloy layer. This plating method, not only has the characteristics of corrosion resistance of galvanized wire, and because of the zinc iron alloy layer. It also has strong corrosion resistance that can not be compared with electric galvanizing. Therefore, this plating method is particularly suitable for a variety of strong acid, alkali fog and other strong corrosive environment.

Stainless steel is short for rust acid steel, air, steam, water and other weak corrosion medium or stainless steel is called stainless steel; And the chemical corrosion resistance medium (acid, alkali, salt and other chemical etching) corrosion of steel called acid steel.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

(8) galvanized wire coated hexagonal mesh is coated with a layer of PVC protective layer on the surface of galvanized iron wire, and then woven into a variety of specifications of hexagonal mesh. This layer of PVC protective layer will greatly increase the service life of the net, and through the choice of different colors, so that it can be integrated with the surrounding natural environment.

2, galvanized silk mesh molding sheet storage ground should be flat, according to the symbolic needs of regular accumulation, height should not exceed 2M, and away from the heat source, avoid exposure.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

We must have a certain understanding of the hexagonal network, we are the beautiful appearance of the hexagonal network, hexagonal network is not only very beautiful appearance, in fact, the practical value of survival is very high. To introduce the relevant information should be very clearly know the highway guardrail net, hexagonal wire netting in all kinds of fence netting, in the value of the high-speed on the road more MaoJian, it not only be used in all kinds of road, in a sports ball games venue and try our best to take care of landslides, also has reached very matter effectiveness.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

This process has no mold, low processing cost, easy forming, can process a variety of shapes and other characteristics are widely used. But the products of the guardrail are powder impregnated plastic. According to whether it needs heating, it is divided into hot dipping and cold dipping. According to the raw materials of dipping, it can be divided into liquid dipping and powder dipping. Hot-dip galvanizing, as a metal anticorrosion method, is usually to put the steel structure to be derusted into the zinc liquid at about 500℃, so that the zinc layer is attached to the surface of the steel structure.

Cold wire drawing is mainly used in the production of hardened low carbon steel wire, with a diameter of 8 mm steel bar to play a fixed role in the development of the construction industry has played a role in promoting the development of the construction industry, widely used. The bonding and anchorage performance between cold wire drawing and concrete is good. When used in components, the phenomenon of cracking in the anchorage area of components and damage caused by steel wire slip is fundamentally eliminated, and the bearing capacity and anti-cracking capacity of the end of components are improved.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.