If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Therefore, when the zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms are diffused with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with the iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with the zinc and sinks into the bottom of the hot galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

The duration of the protective effect of galvanized layer on large roll galvanized wire is closely related to the coating thickness. Generally speaking, in the dry main gas and indoor use, the thickness of galvanized layer only 6-12μm, and in the environment is more severe conditions, galvanized layer thickness needs 20μm “to be up to 50μm”. Therefore, the influence of environment should be considered when choosing the thickness of galvanized layer.

Hexagonal twist flower network is divided into heavy hexagonal network and small hexagonal network two categories. Both are made of steel wire braided with various materials, the difference is that the former uses thicker steel wire, and the latter uses finer steel wire braided.