barbed wire by the foot

Large coil galvanized wire in the zinc immersion distance debugging, keep the original speed unchanged, according to t= KD to determine the zinc immersion time (1), where: t is the zinc immersion time is constant, take 4-7D is the diameter of steel wire mm, and then estimate the zinc immersion distance. By adjusting the zinc dip distance, the zinc dip time of steel wire of various specifications can be shortened by 5s on average. In this way, the zinc consumption per ton of steel wire decreases from 61kg to 59.4kg.

The application of electric welding net is more widely, at present it has replaced the use of other parts of the wire mesh, the cost of electric welding net is lower, the production speed is very fast, so it is very popular. Welding net galvanized before the need for processing is recrystallization annealing, because the welding net must maintain a no oxide and no other impurities of pure iron active surface, if you can not keep its surface clean will lead to a bad galvanizing effect, galvanized layer and iron material is not closely combined, so this step is necessary.

During this process, each time the wire is pulled over, the surface hardens due to the high friction temperature. So basically every time you pull it you have to annealing it in the furnace. On the one hand, it is to reduce the surface hardness. On the other hand, during the process of wire pulling, only the surface is deformed, and the center is unchanged. So there’s a lot of stress inside. Therefore, it is necessary to rely on annealing to eliminate the internal stress, so that the wire becomes soft again to eliminate the stress before being drawn again.