high tensile galvanised wire

Galvanized iron wire is divided into hot galvanized wire and cold galvanized wire, using low carbon steel wire processing, after drawing molding, pickling rust removal, high temperature annealing, hot galvanized, cooling and other processes. It has good toughness and elasticity, and the amount of zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Galvanized iron wire can be cut off in the construction of the tie wire, the length of 20cm, 30cm and 40cm, can be cut off according to requirements.

Steel mesh plastic sprayed: Coating is also we often speak of electrostatic powder spraying coating, it is to make plastic powder charged with static electricity generator, adsorption in the iron plate or other product appearance, and then through 180 ~ 220 ℃ baking, make powder agglomeration adhesion of metal or other objects, plastic product used for indoor use more boxes, paint film present flat or matte effect. Spray powder mainly acrylic powder, polyester powder and so on.

There is also a scaly or boride film or oxide. To remove the photosynovium or oxide commonly used methods are: lead grease removal method, acoustic cleaning method, alkali washing or pickling electrolysis grease to oxide method, these methods in the use of gas or steam harmful to human body, pollution, not environmental protection.

Stainless steel wire drawing is a metal working (stainless steel) process, is a popular surface treatment technology in the stainless steel and aluminum products industry today. It is the effect of drawing stainless steel and aluminum products. So galvanized wire and stainless steel wire are two different products. Defects such as surface film and surface inclusion can be found and treated by conventional techniques in order to locally remove the surface film and surface inclusion from the surface of galvanized iron wire. Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank.

Thus, when zinc is sufficient in a solid melt, the two atoms of zinc and iron disperse with each other. The zinc atoms in the iron matrix are moved into the lattice of the matrix, and the iron elements are gradually formed into alloys. The zinc composition of iron and intermetallic compound FeZn13 in molten zinc solution and the bottom of hot galvanized sheet can be used as zinc slag. The pure zinc layer composed of zinc leaching solution is hexagonal crystal.