If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.

In fact, iron wire has been widely used in our daily life, and it has very good performance. Iron wire production developed earlier because of its simple technology and wide application. Plastic spraying refers to the plastic powder, sprayed on the product of a surface treatment method. Plastic spraying is often referred to as electrostatic powder spraying, the use of electrostatic generator to make plastic powder charged, adsorbed on the surface of the iron plate, and then after 180 ~ 220℃ baking, so that the powder melt and adhere to the metal surface, plastic spraying products are used for indoor use of the box, paint film showing flat or matte effect.

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be brought out. Hot dip galvanizing is an effective way to prevent corrosion of metal. It is mainly used for metal structure facilities in various industries. It is to immerse the steel parts after rust removal into the melting zinc liquid at about 500℃, so that the surface of the steel members is attached with zinc layer, so as to play the purpose of anti-corrosion. The galvanized layer is more firm.

The blade thorn rope is formed by the punching steel plate and mechanically rolled on the steel wire. The width of the blade is 22mm, the vertical distance between the two blades is 15mm, the longitudinal distance between the blade is 34mm, and the diameter of the core wire is 2.5mm. The blade is made of Q195 steel plate with 0.5mm thickness.