The spring steel wire is made of high carbon and high quality carbon structural steel or carbon tool steel wire rod, and its chemical composition, gas content and non-metallic inclusion must be strictly controlled according to the use of the spring. In order to reduce the appearance of shortcomings and decarbonization layer, the consumption of rod billet to stop surface grinding, if necessary, but also stop peeling.

Galvanizing can be done by zincate galvanizing or chloride galvanizing. Appropriate additives shall be used to obtain a coating that meets the requirements of this standard. Luminescence treatment should be carried out after luminescence plating. The parts that need to be dehydrogenated for passivation should be passivated after dehydrogenation. Before passivation, 1%H2SO4 or 1% hydrochloric acid should be applied to activate 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

Galvanized wire in acid, alkali, sodium chloride aqueous solution of poor corrosion resistance, in the atmosphere containing carbon dioxide and hydrogen sulfide, as well as Marine atmosphere is not corrosion resistance. In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded. Galvanized wire and general wire is very different, general wire is cheap, and because the iron is not very stable, easy to rust in the wet place, so the stability is not very good, the life is not very long.

The posts are the sturdy vertical structures that anchor the fence to the ground. They are vital for maintaining the integrity and alignment of the entire fencing system. Posts should be made from robust materials, often the same wrought iron used for the pickets, and are typically set into concrete for added stability. Depending on the design, posts may include decorative caps or finials, adding an extra flair to the overall appearance.