Operating procedures: When using cold galvanized wire, all tools and stacked objects obstructing activities should be removed from the work site and equipment. When pickling, put the wire into the cylinder slowly to prevent acid splashing on the body. When adding acid, it is necessary to pour the acid into the water slowly. It is forbidden to pour the water into the acid to prevent the acid from splashing out. Wear protective glasses when working. Do not push or beat cold galvanized wire and other articles when handling them.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

Cold plating is a physical treatment method, the zinc is simple and uneven, the amount of zinc is also less than in the corrosion and rust prevention and chemical disposal of hot plating; The amount of hot zinc plating is relatively thick, the surface of the disposal is flat on average, and it is not easy to fall off. A layer of alloy composed of zinc and metal has very strong oxidation ability, and there is a layer of pure zinc on the outside of this layer of alloy, which is why hot plating is thicker and stronger than cold plating. Under the condition of high degree of natural recovery, galvanized hook net can play a very good maintenance effect on the environment, it is not afraid of wind and rain, it is the battle machine in the hook net, much stronger than the dip plastic hook net.

Two, cold galvanized wire production process of galvanized. Galvanizing is the core process in the production of cold galvanized wire, mainly by soaking the steel wire in a molten zinc solution to form a zinc layer on its surface.