cattle wire mesh fencing

Greenhouse special electroplating process iron wire blackening solution:

The life of the “wire”, is actually “low carbon steel wire”, carbon content in less than 0.2%. The surface is usually coated with zinc plating because it is easy to rust. Under atmospheric conditions, the galvanized layer will not rust before most of the fall off, relatively soft. The life of the “steel wire”, is carbon content in about 0.6% of the “carbon steel wire”, or carbon content in about 0.8% of the “high carbon steel wire”, they have enough hardness and elasticity after appropriate heat treatment, high strength. Uses such as winding ordinary spring and so on.

Using the patented technology of the invention, regularly put zinc block into the plating aid pool, so that the bivalent iron in the plating aid into trivalent iron, and play a stable PH value in a numerical range of an important measure, but also easy to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

Even so, when they come out, they make trouble, even though they know they will be punished, but they are only in a cage.) If you have time to refer to some foreign dog books, also strongly advocate cage training as a puppy. Before starting cage training, the cage is padded with a water bottle, some fun toys and bones to chew on. The cage door must be opened. Order the dog into the cage, then lure it into its new den with tasty cookies.

Some customers are just for ordinary fencing, but the pictures provided to the barbed rope factory are indeed applied to the barbed rope products in prison, maybe because the customers prefer the style, but such products are really a little overqualified to be installed in ordinary areas. Even if the customers prefer such barbed rope products, the higher price is prohibitive. The price and quality of the prison rope are certainly not the level of the rope we contact in our daily life.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Blade thorn rope because the volume is relatively large, so the thorn rope factory is used to packaging treatment.

Hot dip galvanizing is dipped in zinc liquid melted by heating, with fast production speed and thick but uneven coating. The market allows a low thickness of 45 microns and a high of more than 300 microns. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Application range of hot dip galvanizing: because the coating is thicker, hot dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for iron and steel parts in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, Marine exploration, metal structure, power transmission, shipbuilding and other industries, in the field of agriculture such as sprinkler irrigation, greenhouse and construction industry such as water and gas transmission, wire casing, scaffolding, Bridges, highway guardrail and other aspects, has been widely used.

Hardness is a commonly used property index in mechanical properties of metal materials. The iron wire factory introduces a fast and economical test method for hardness testing. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad. In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting.

Some customers just use ordinary fences, but the pictures provided to the barbed rope factory are really used in the barbed rope products of prison, maybe because the customers prefer the style, but such products are really a little overqualified to be installed in ordinary areas. Even if customers prefer such barbed rope products, the high price is also prohibitive. The price and quality of the prison application barbed rope is certainly not the level of the barbed rope we contact in daily life.

The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.