(3) For some use of special paint spraying should be baked, of course, depending on the size of the area, small can be placed in the oven, large can only be dried first, and then to dry parts for processing, lock baking, if other circumstances can only use high temperature tools bit by bit baking. The products that can be baked in the oven should be leveled at room temperature for 15 to 30 minutes, baked at a low temperature of 60 degrees Celsius for half an hour, and then baked at the reserved baking temperature for one and a half hours, and then cooled down.

The duration of the protective effect of galvanized layer on large roll galvanized wire is closely related to the coating thickness. Generally speaking, in the dry main gas and indoor use, the thickness of galvanized layer only 6-12μm, and in the environment is more severe conditions, galvanized layer thickness needs 20μm “to be up to 50μm”. Therefore, the influence of environment should be considered when choosing the thickness of galvanized layer.

The welding process of galvanized steel wire mesh because of low carbon steel carbon content is low, manganese and silicon content is low, will not occur severe hardening or quenching structure due to welding. The low carbon steel joints have excellent plasticity and impact toughness after welding. In the welding process, it is generally not necessary to preheat, interlayer temperature control, post-heating control and heat treatment to improve the welding structure.

The size of the galvanized layer of galvanized iron wire is related to the anti-corrosion ability and application effect of galvanized wire. The thickness of the galvanized layer of the general standard galvanized wire products should be tested after the product is formed. There are three specific test methods. Weighing method and cross section microscopy method are destructive experimental methods, and magnetic method is a relatively rigorous non-destructive method, but the measurement steps and requirements are relatively high, so they are rarely used in specific applications. The first two methods are intuitive and common methods.