3. Galvanizing: the preheated steel wire is immersed in the molten zinc liquid, so that the surface is attached with a zinc layer. The control of galvanizing time and temperature has great influence on the quality of zinc layer.

Because of the high carbon content, simple cracks occur during water quenching, so double liquid quenching (water quenching + oil cooling) is mostly used, and oil quenching is mostly used for small cross section parts. This type of steel is generally used after quenching by medium temperature tempering or normalizing or in the surface quenching state. Mainly used for manufacturing spring and wear-resistant parts.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

There is good toughness and elasticity, simply put, can be easily made into various shapes, and zinc as a coating is silver, very beautiful. Such characteristics make hot dip galvanized wire handicrafts, woven screen and other aspects have also been applied. Hot plating wire selection of high quality low carbon steel rod processing, is the selection of high quality low carbon steel, after drawing molding, pickling rust removal, high temperature annealing, cooling and other processes.